Jiang Haoyang, Xiong Feng, Qin Mulin, Gao Song, He Liuruyi, Zou Ruqiang. Conductive Phase Change Materials (PCMs) for Electro-to-Thermal Energy Conversion, Storage and Utilization[J]. Progress in Chemistry, 2023, 35(3): 360-374.
Conductive filler | PCMs | Filler content (wt%) | ( ℃) | Latent heat (J/g) | λW/(m·k) | σb (S/m) | The trigger voltagec (V) | ηd (%) | The working voltage e (V) | ref |
---|---|---|---|---|---|---|---|---|---|---|
acetylene black | PEG2000· CaCl2 | 20 | 51.48 | 78.5 | 1.2 | 3.3 | 1.5 | 29.7 | 1.5 | |
acetylene black | PEG2000· CaCl2 | 20 | 51.48 | 78.5 | 1.2 | 3.3 | 1.5 | 64.7 | 2.5 | |
carbon nanofiber | paraffin wax | 2 | 70 | - | - | 0.2 | - | - | - | |
single-wall CNT | hexadecyl acrylate | - | 36.7 | 52 | 0.4675 | 718 | - | - | - | |
multi-wall CNT | hexadecyl acrylate | - | 38 | 40 | 0.877 | 389 | - | - | - | |
CNTs | PEG2000- CaCl2 | 20 | 49.72 | 89.81 | 0.91 | 0.01 | - | 58.3 | 1.5 | |
CNTs | PEG2000- CaCl2 | 20 | 49.72 | 89.81 | 0.91 | 0.01 | - | 70.2 | 2 | |
expanded graphite | PEG2000- CaCl2 | 6 | 49.3 | 107.5 | 3.73 | 0.2 | 2 | 48.2 | 2 | |
expanded graphite | PEG2000- CaCl2 | 6 | 49.3 | 107.5 | 3.73 | 0.2 | 2 | 86.9 | 5 | |
expanded graphite | Methyl stearate | 15 | 33.4 | 147 | 3.6 | - | 1.4 | 47 | 1.4 | |
expanded graphite | Methyl stearate | 15 | 33.4 | 147 | 3.6 | - | 1.4 | 72 | 1.7 | |
expanded graphite | N-eicosane | 15 | 36.41 | 199.4 | 3.56 | - | 1.9 | 65.7 | 2.1 | |
expanded graphite | N-eicosane | 30 | 36.31 | 163.5 | 4.21 | - | 1.9 | 42.9 | 2.1 | |
expanded graphite | paraffin | 20 | 56.2 | 120 | 1.38 | 5 | - | - | - | |
expanded graphite | paraffin | 70 | 43.05 | 47.76 | 19.27 | 4545 | - | - | 4.4 | |
graphene | Hexadecyl acrylate | - | 32.7 | 57 | 3.957 | 219 | - | - | 30 | |
graphene oxide/CNT | PEG1000 | 22 | 37.24 | 110.7 | 0.45 | - | 5.8 | 70 | 6.6 | |
graphene oxide/CNT | docosane | 3.3 | 38.1 | 240.8 | - | 52.63 | - | - | - | |
graphene/ PANI | PEG20000 | - | 57.93 | 115.97 | - | - | - | - | - | |
CNT/PU/ PDA/ PEDOT:PSS | paraffin wax | - | 20 | 106.86 | - | - | - | 42.92 | 3 | |
CNT/PU/ PDA/ PEDOT:PSS | paraffin wax | - | 20 | 106.86 | - | - | - | 91.03 | 4.2 | |
CNT/PU/Ag nanoflower | Lauric acid | - | 46 | 124.5 | 0.479 | 190 | - | 70.1 | 20 | |
cotton/ stainless steel wire | PEG | - | 53.53 | 33.46 | 0.281 | - | - | - | - | |
Ti3C2 MXene nanosheets | PEG4000 | 22.5 | 60 | 131.2 | 2.052 | 10.41 | - | - | 7.2 |
Conductive framework | PCMS | Filler content (wt%) | Tm ( ℃) | Latent heat (J/g) | λ W/(m·k) | σ (S/m) | The trigger voltage (V) | η (%) | The working voltage(V) | ref |
---|---|---|---|---|---|---|---|---|---|---|
carbon foam | PEG6000 | - | 62.82 | 163.9 | - | - | - | 85 | 3.6 | |
carbon foam | paraffin wax | - | 57.05 | 120.2 | - | - | - | 74 | 3.6 | |
carbon foam | PU(PEG6000) | 33.3 | 43.2 | 61.9 | 0.48 | - | 0.8 | 75 | 1.1 | |
carbon fiber scaffold | paraffin wax | 15 | 39.22 | 182.22 | 0.424 | 19.6 | 2 | 81.1 | 3 | |
carbon aerogel | paraffin wax | 5 | 53.5 | 115.2 | - | 3.4 | - | 71.4 | 15 | |
cotton cloth/TPU | paraffin wax | 50.75 | 34.13 | 93.5 | - | 296.68 | 3 | 67.39 | 4 | |
CNT sponge | paraffin wax | 13 | 24 | 131.7 | 1.2 | - | 1.5 | 52.5 | 1.75 | |
CNT sponge | PU | 10 | 59.41 | 132.02 | 2.4 | - | 1.3 | 94 | 2 | |
CNT array | n-eicosane | 10 | 34 | 217.3 | - | - | 1 | 74.7 | 1.3 | |
single-wall CNT scaffold | eicosane | 27.1 | 36.7 | 204.8 | - | 620.3 | 3 | 80.1 | 4 | |
single-wall CNT scaffold | eicosane | 27.1 | 36.7 | 204.8 | - | 620.3 | 3 | 91.3 | 5 | |
graphite foam | Paraffin wax | 20 | 50.2 | 174.2 | 1.38 | - | - | 74.6 | 5 | |
graphite foam | PU(PEG4000) | 18 | 41 | 64.5 | 3.5 | - | - | 69 | 1.4 | |
graphite foam | PU(PEG6000) | 18 | 42.5 | 76.1 | 3.6 | - | - | 85 | 1.4 | |
graphite foam | PU(PEG8000) | 18 | 46.1 | 80.3 | 3.4 | - | - | 45 | 1.4 | |
graphite foam | PU(PEG6000) | 27 | 43.8 | 60.3 | 10.86 | - | 1.5 | 85 | 1.8 | |
graphite foam/MPU | octadecanol | 52.5 | 56.1 | 130 | 5.55 | - | - | 61.4 | - | |
graphite nanoplatelets | Pentaerythritol | 20 | 186 | 225.3 | 27 | 32 300 | 0.22 | 92.73 | 0.34 | |
3D reduced graphene/ carbon scaffold | paraffin wax | 20 | 39.53 | 157 | 33.5 | 294.9 | - | 88 | - | |
3D reduced graphene/ BN scaffold | PEG10000 | 15.2 | 59.5 | 164.1 | 0.59 | - | - | 87.9 | 7 | |
graphene aerogel | paraffin wax | 3 | 57 | 202.2 | 1.06 | - | - | - | - | |
graphene aerogel | Paraffin | 6 | 46.05 | 193.7 | 0.248 | 258.7 | 1 | 85.4 | 3 | |
graphene aerogel/ZnO | PU (PEG4000) | 2.29 | 57.1 | 108.1 | 2.99 | - | - | 84.4 | 15 | |
graphene aerogel/halloysite nanotubes | PU | 1.17 | 57.4 | 103.3 | - | - | 66.3 | 10 | ||
reduced graphene oxide aerogel/SEBS | paraffin wax | 6.47 | 40.19 | 226.3 | - | - | - | - | 8 | |
graphene nanoplatelets/ cellulose aerogel | PEG 6000 | 1.51 | 67.6 | 182.6 | 0.43 | - | - | - | - | |
graphene nanoplatelet/ cellulose nanofiber hybrid- coated melamine foam | PEG 6000 | 4.8 | 61.7 | 178.9 | 1.03 | 6.19 | - | 66.13 | 20 | |
MOF-derived carbon/ graphene oxide aerogel | lauric acid | - | 51 | 140 | 0.26 | - | 2.2 | 90 | 2.2 | |
ZIF@MOF-C/CNT | octadecane | 30 | 31.9 | 135.9 | 1.35 | 526.32 | - | 94.5 | 1.1 | |
copper nanowire aerogels | paraffin | 1.95 | 53 | 173.2 | - | 14 | - | - | - | |
CNTs nanoarray/nickel foam | 1-hexadecanamine | - | 50.38 | 132.2 | 0.277 | - | - | - | 30 | |
PEDOT:PSS/MXene framework | PEG20000 | 1.22 | 61.6 | 237.6 | 0.215 | 0.86 | - | - | 30 |
Conductive polymer | PCMS | Filler content (wt%) | Tm ( ℃) | Latent heat (J/g) | λW/ (m·K) | σ (S/m) | The trigger voltage(V) | η (%) | The working voltage(V) | ref |
---|---|---|---|---|---|---|---|---|---|---|
PPy/crosslinked polystyrene | paraffin wax | - | 44.9 | 114.2 | - | 420 | 1.8 | 63.2 | 1.8 | |
PPy/crosslinked polystyrene | paraffin wax | - | 44.9 | 114.2 | - | 420 | 1.8 | 80.1 | 3 | |
PPy/ polydivinylbenzene nanotubes | paraffin wax | 27.1 | 30 | 145.7 | - | 55.6 | - | 66.8 | 2.2 | |
PPy/ polydivinylbenzene nanotubes | paraffin wax | 27.1 | 30 | 145.7 | - | 55.6 | - | 89.6 | 2.5 | |
PPy/Cellulose nanofiber | PEG | 6 | 57.41 | 169.7 | - | - | 1.75 | 76.6 | 1.75 | |
PPy/Cellulose nanofiber | PEG | 6 | 57.41 | 169.7 | - | - | 1.75 | 85.1 | 1.9 | |
PPy/melamine- formaldehyde | n-octadecane | 50.3 | 30 | 90.2 | - | 0.33 | - | - | - | |
PPy/PU | PEG | 60.8 | 47.5 | 62.8 | - | 1184 | - | - | - |
[1] |
Sundararajan S, Samui A B, Kulkarni P S. J. Mater. Chem. A, 2017, 5(35): 18379.
doi: 10.1039/C7TA04968D |
[2] |
Zhang Y A, Umair M M, Zhang S F, Tang B T. J. Mater. Chem. A, 2019, 7(39): 22218.
doi: 10.1039/C9TA06678K |
[3] |
Henry A, Prasher R, Majumdar A. Nat. Energy, 2020, 5(9): 635.
doi: 10.1038/s41560-020-0675-9 |
[4] |
Su W G, Darkwa J, Kokogiannakis G. Renew. Sustain. Energy Rev., 2015, 48: 373.
doi: 10.1016/j.rser.2015.04.044 |
[5] |
Aftab W, Usman A, Shi J M, Yuan K J, Qin M L, Zou R Q. Energy Environ. Sci., 2021, 14(8): 4268.
doi: 10.1039/D1EE00527H |
[6] |
Aydin D, Casey S P, Riffat S. Renew. Sustain. Energy Rev., 2015, 41: 356.
doi: 10.1016/j.rser.2014.08.054 |
[7] |
Hyun D C, Levinson N S, Jeong U, Xia Y N. Angew. Chem. Int. Ed., 2014, 53(15): 3780.
doi: 10.1002/anie.201305201 |
[8] |
Liu W, Zhang X L, Ji J, Wu Y F, Liu L. Energy Technol., 2021, 9(7): 2100169.
|
[9] |
Tahan Latibari S, Sadrameli S M. Sol. Energy, 2018, 170: 1130.
doi: 10.1016/j.solener.2018.05.007 |
[10] |
Kalidasan B, Pandey A K, Shahabuddin S, Samykano M, Thirugnanasambandam M, Saidur R. J. Energy Storage, 2020, 27: 101118.
|
[11] |
Wang W T, Tang B T, Ju B Z, Gao Z M, Xiu J H, Zhang S F. J. Mater. Chem. A, 2017, 5(3): 958.
doi: 10.1039/C6TA07144A |
[12] |
Wang W T, Fan X Q, Qiu J J, Umair M M, Ju B Z, Zhang S F, Tang B T. Chem. Eng. J., 2018, 358.
|
[13] |
Fan X Q, Xiao J Q, Wang W T, Zhang Y A, Zhang S F, Tang B T. Polymers, 2018, 10(6): 585.
doi: 10.3390/polym10060585 |
[14] |
Horsfield A P, Bowler D R, Fisher A J, Todorov T N, Montgomery M J. J. Phys.: Condens. Matter, 2004, 16(21): 3609.
|
[15] |
Zhang H Q, Sun Q R, Yuan Y P, Zhang Z J, Cao X L. Chem. Eng. J., 2018, 336: 342.
doi: 10.1016/j.cej.2017.12.046 |
[16] |
Zhang K, Han B G, Yu X. Energy Convers. Manag., 2012, 64: 62.
doi: 10.1016/j.enconman.2012.06.021 |
[17] |
Cao R R, Chen S, Wang Y Z, Han N, Liu H H, Zhang X X. Carbon, 2019, 149: 263.
doi: 10.1016/j.carbon.2019.04.005 |
[18] |
Sun Q R, Zhang N, Zhang H Q, Yu X P, Ding Y L, Yuan Y P. Renew. Energy, 2020, 145: 2629.
doi: 10.1016/j.renene.2019.08.007 |
[19] |
Sun Q R, Zhang N, Yu X P, Ju F L, Szilágyi I M, Yuan Y P. Int. J. Energy Res., 2021, 45(5): 7675.
doi: 10.1002/er.v45.5 |
[20] |
Tabassum H, Huang X Y, Chen R J, Zou R Q. J. Materiomics, 2015, 1(3): 229.
doi: 10.1016/j.jmat.2015.07.002 |
[21] |
Li C C, Zhang B, Liu Q X. J. Energy Storage, 2020, 29: 101339.
|
[22] |
Frᶏc M, PichÓr W, Szołdra P, Szudek W. Constr. Build. Mater., 2021, 275: 122126.
|
[23] |
Luo M Y, Song J Q, Ling Z Y, Zhang Z G, Fang X M. Mater. Today Energy, 2021, 20: 100652.
|
[24] |
Cao R R, Wang Y Z, Chen S, Han N, Liu H H, Zhang X X. ACS Appl. Mater. Interfaces, 2019, 11(9): 8982.
doi: 10.1021/acsami.8b18282 |
[25] |
Guo X F, Liu C, Li N, Zhang S D, Wang Z Y. Ind. Eng. Chem. Res., 2018, 57(46): 15697.
doi: 10.1021/acs.iecr.8b03093 |
[26] |
Zheng Z L, Jin J D, Xu G K, Zou J L, Wais U, Beckett A, Heil T, Higgins S, Guan L H, Wang Y, Shchukin D. ACS Nano, 2016, 10(4): 4695.
doi: 10.1021/acsnano.6b01104 |
[27] |
Yu C B, Youn J R, Song Y S. Fibers Polym., 2019, 20(3): 545.
doi: 10.1007/s12221-019-1067-2 |
[28] |
Wu J J, Wang M X, Dong L, Shi J, Ohyama M, Kohsaka Y, Zhu C H, Morikawa H. ACS Nano, 2022, 16(8): 12801.
doi: 10.1021/acsnano.2c04971 |
[29] |
Niu Z X, Qi S Y, Shuaib S S A, Yuan W Z. Compos. B Eng., 2022, 228: 109431.
|
[30] |
Yu L X, Qin X H, Ke G Z, Tang J N, Wang Y. Compos. Commun., 2022, 32: 101152.
doi: 10.1016/j.coco.2022.101152 |
[31] |
Lu X, Huang H W, Zhang X Y, Lin P C, Huang J T, Sheng X X, Zhang L, Qu J P. Compos. B Eng., 2019, 177: 107372.
doi: 10.1016/j.compositesb.2019.107372 |
[32] |
Janas D, Koziol K K. Nanoscale, 2014, 6(6): 3037.
doi: 10.1039/c3nr05636h pmid: 24519536 |
[33] |
Wu Y P, Wang T. Energy Convers. Manag., 2015, 101: 164.
doi: 10.1016/j.enconman.2015.05.006 |
[34] |
Nat. Nanotechnol. 2010, 5: 755.
|
[35] |
Wang J F, Shen M M, Liu Z X, Wang W J. Nano Energy, 2022, 97: 107177.
doi: 10.1016/j.nanoen.2022.107177 |
[36] |
Maleki M, Karimian H, Shokouhimehr M, Ahmadi R, Valanezhad A, Beitollahi A. Chem. Eng. J., 2019, 362: 469.
doi: 10.1016/j.cej.2019.01.032 |
[37] |
Wu W H, Huang X Y, Yao R M, Chen R J, Li K, Zou R Q. Acta Phys. Chim. Sin. 2017, 33(1): 255.
doi: 10.3866/PKU.WHXB201610181 |
[38] |
Umair M M, Zhang Y A, Tehrim A, Zhang S F, Tang B T. Ind. Eng. Chem. Res., 2020, 59(4): 1393.
doi: 10.1021/acs.iecr.9b06288 |
[39] |
Li Y Q, Samad Y A, Polychronopoulou K, Alhassan S M, Liao K. J. Mater. Chem. A, 2014, 2(21): 7759.
doi: 10.1039/C4TA00839A |
[40] |
Umair M M, Zhang Y A, Zhang S F, Jin X, Tang B T. J. Mater. Chem. A, 2019, 7(46): 26385.
doi: 10.1039/C9TA09088F |
[41] |
Chen L J, Zou R Q, Xia W, Liu Z P, Shang Y Y, Zhu J L, Wang Y X, Lin J H, Xia D G, Cao A Y. ACS Nano, 2012, 6(12): 10884.
doi: 10.1021/nn304310n |
[42] |
Aftab W, Mahmood A, Guo W H, Yousaf M, Tabassum H, Huang X Y, Liang Z B, Cao A Y, Zou R Q. Energy Storage Mater., 2019, 20: 401.
|
[43] |
Liu Z P, Zou R Q, Lin Z Q, Gui X C, Chen R J, Lin J H, Shang Y Y, Cao A Y. Nano Lett., 2013, 13(9): 4028.
doi: 10.1021/nl401097d |
[44] |
Chen R J, Huang X Y, Deng W B, Zheng R Z, Aftab W, Shi J M, Xie D L, Zou R Q, Mei Y. Appl. Energy, 2020, 260: 114320.
doi: 10.1016/j.apenergy.2019.114320 |
[45] |
Liu M Y, Zhang X G, Liu X J, Wu X W, Ye X J, Qiao J X, Sun Z H, Zhu X, Huang Z H. ACS Sustainable Chem. Eng., 2022, 10(24): 8051.
doi: 10.1021/acssuschemeng.2c02125 |
[46] |
Chen R J, Yao R M, Xia W, Zou R Q. Appl. Energy, 2015, 152: 183.
doi: 10.1016/j.apenergy.2015.01.022 |
[47] |
Wu W H, Huang X Y, Li K, Yao R M, Chen R J, Zou R Q. Appl. Energy, 2017, 190: 474.
doi: 10.1016/j.apenergy.2016.12.159 |
[48] |
Wu W H, Yao R M, Huang X Y, Chen R J, Li K, Gao S, Zou R Q. Mater. Chem. Front., 2017, 1(7): 1430.
doi: 10.1039/C6QM00381H |
[49] |
Wu M Q, Li T X, Wang P F, Wu S, Wang R Z, Lin J. Small, 2022, 18(9): 2105647.
|
[50] |
Li T X, Wu M Q, Wu S, Xiang S Z, Xu J X, Chao J W, Yan T S, Deng T, Wang R Z. Nano Energy, 2021, 89: 106338.
|
[51] |
Umair M M, Zhang Y A, Zhang S F, Jin X, Tang B T. Sustain. Energy Fuels, 2020, 4(8): 4285.
|
[52] |
Yang G Q, Zhao L Y, Shen C F, Mao Z P, Xu H, Feng X L, Wang B J, Sui X F. Sol. Energy Mater. Sol. Cells, 2020, 209: 110441.
|
[53] |
Ye S B, Zhang Q L, Hu D D, Feng J C. J. Mater. Chem. A, 2015, 3(7): 4018.
doi: 10.1039/C4TA05448B |
[54] |
Li G Y, Zhang X T, Wang J, Fang J H. J. Mater. Chem. A, 2016, 4(43): 17042.
doi: 10.1039/C6TA07587H |
[55] |
Zhou Y, Wang X J, Liu X D, Sheng D K, Ji F C, Dong L, Xu S B, Wu H H, Yang Y M. Sol. Energy Mater. Sol. Cells, 2019, 193: 13.
doi: 10.1016/j.solmat.2018.12.041 |
[56] |
Zhou Y, Wang X J, Liu X D, Sheng D K, Ji F C, Dong L, Xu S B, Wu H H, Yang Y M. Carbon, 2019, 142: 558.
doi: 10.1016/j.carbon.2018.10.083 |
[57] |
Cai Y X, Zhang N, Yuan Y P, Zhong W, Yu N Y. Sol. Energy Mater. Sol. Cells, 2021, 233: 111390.
doi: 10.1016/j.solmat.2021.111390 |
[58] |
Wei X, Xue F, Qi X D, Yang J H, Zhou Z W, Yuan Y P, Wang Y. Appl. Energy, 2019, 236: 70.
doi: 10.1016/j.apenergy.2018.11.091 |
[59] |
Wu H Y, Deng S, Shao Y W, Yang J H, Qi X D, Wang Y. ACS Appl. Mater. Interfaces, 2019, 11(50): 46851.
doi: 10.1021/acsami.9b16612 |
[60] |
Wang M, Zhang C, Wang J Z, Wang Y, Yu F Q. J. Energy Storage, 2022, 52: 104905.
|
[61] |
Li A, Dong C, Dong W J, Yuan F G, Gao H Y, Chen X, Chen X B, Wang G. Adv. Electron. Mater., 2020, 6(6): 1901428.
|
[62] |
Zhang L, An L, Wang Y H, Lee A, Schuman Y, Ural A, Fleischer A S, Feng G. Chem. Eng. J., 2019, 373: 857.
doi: 10.1016/j.cej.2019.05.104 |
[63] |
Cao X Y, Yang L J, Cui J, Feng Q B, Wang C J, Zhu Z Q, Sun H X, Li J Y, Liang W D, Li A. Colloids Surf. A Physicochem. Eng. Aspects, 2022, 651: 129516.
doi: 10.1016/j.colsurfa.2022.129516 |
[64] |
Jin X Z, Yang Z Y, Huang C H, Yang J H, Wang Y. Chem. Eng. J., 2022, 448: 137599.
doi: 10.1016/j.cej.2022.137599 |
[65] |
Paul J, Pandey A K, Mishra Y N, Said Z, Mishra Y K, Ma Z J, Jacob J, Kadirgama K, Samykano M, Tyagi V V. Renew. Sustain. Energy Rev., 2022, 161: 112321.
doi: 10.1016/j.rser.2022.112321 |
[66] |
Inagaki M, Qiu J S, Guo Q G. Carbon, 2015, 87: 128.
doi: 10.1016/j.carbon.2015.02.021 |
[67] |
Kim J H, Jeong E, Lee Y S. J. Ind. Eng. Chem. 2015, 32: 21.
doi: 10.1016/j.jiec.2015.09.003 |
[68] |
Wu S, Li T X, Tong Z, Chao J W, Zhai T Y, Xu J X, Yan T S, Wu M Q, Xu Z Y, Bao H, Deng T, Wang R Z. Adv. Mater., 2019, 31(49): 1905099.
|
[69] |
Kashyap S, Kabra S, Kandasubramanian B. J. Mater. Sci., 2020, 55(10): 4127.
doi: 10.1007/s10853-019-04325-7 |
[70] |
Aftab W, Huang X Y, Wu W H, Liang Z B, Mahmood A, Zou R Q. Energy Environ. Sci., 2018, 11(6): 1392.
doi: 10.1039/C7EE03587J |
[71] |
Chen X, Gao H Y, Yang M, Xing L W, Dong W J, Li A, Zheng H Y, Wang G. Energy Storage Mater., 2019, 18: 349.
|
[72] |
Chen X, Gao H Y, Tang Z D, Wang G. Cell Rep. Phys. Sci., 2020, 1(10): 100218.
|
[73] |
Cheng L Q, Kong L B, Zhang X, Kong X F. Sol. Energy Mater. Sol. Cells, 2022, 235: 111461.
doi: 10.1016/j.solmat.2021.111461 |
[74] |
Kong L B, Wang Z Y, Kong X F, Wang L, Ji Z Y, Wang X M, Zhang X. ACS Appl. Mater. Interfaces, 2021, 13(25): 29965.
doi: 10.1021/acsami.1c07160 |
[75] |
Chen L Y, Lv J C, Ding L, Yang G Q, Mao Z P, Wang B J, Feng X L, Zapotoczny S, Sui X F. Chem. Eng. J., 2020, 400: 125950.
doi: 10.1016/j.cej.2020.125950 |
[76] |
Yun H R, Li C L, Zhang X X. e-Polymers, 2019, 19(1): 519.
doi: 10.1515/epoly-2019-0055 |
[77] |
Gao M H, Feng W, Qi X D, Wang Y. Chin. J. Polym. Sci., 2022, 40(11): 1380.
doi: 10.1007/s10118-022-2773-6 |
[78] |
Huang Y, Li H F, Wang Z F, Zhu M S, Pei Z X, Xue Q, Huang Y, Zhi C Y. Nano Energy, 2016, 22: 422.
doi: 10.1016/j.nanoen.2016.02.047 |
[79] |
Yan Q S, Du X X, Liu Y, Zhou X, Xin B J. ACS Appl. Mater. Interfaces, 2022, 14(21): 24820.
doi: 10.1021/acsami.2c05155 |
[80] |
Lv J C, Zhou P W, Zhang L P, Zhong Y, Sui X F, Wang B J, Chen Z Z, Xu H, Mao Z P. Chem. Eng. J., 2019, 361: 897.
doi: 10.1016/j.cej.2018.12.083 |
[1] | Lujie Fan, Li Chen, Yin He, Hao Liu. Flexible Pressure/Strain Sensors Based on 3D Conductive Materials [J]. Progress in Chemistry, 2021, 33(5): 767-778. |
[2] | Zhou Jianwei, Yu Dongmei, Zhao Yunhui, Su Junfeng, Yuan Xiaoyan. Organic Alkane Phase Change Materials and Their Microencapsulation [J]. Progress in Chemistry, 2011, 23(4): 695-703. |